Elham Shokri, Reza Yegani & Borhan Ghofrani

Preparation of a new modified clay with amino acid for anionic pollutant removal from water

(Volume 86 - Année 2017 — Special issue)
Article
Open Access

Documento adjunto(s)

Version PDF originale

Abstract

Modified montmorilonite (Mt) as clay mineral with amino acid (M-AA) was synthesized by cation exchange method and used to remove anionic pollutants from water. The modified clay was characterized by X-ray diffraction (XRD) and zeta potential. XRD results showed that aminoacid can be intercalated into the Mt and increase the interlayer space of Mt. Positive zeta potential of modified Mt confirmed the modification of Mt with amino acid. The adsorption of pollutants onto modified Mt as a function of their initial concentration and solution pH was investigated. The removal efficiency was increased with increasing the pollutant initial concentration, however it decreased with increasing pH of solution. The maximum adsorption capacities of modified Mt with amino acid was 5 times larger than unmodified Mt. The regeneration studies were carried out up to 10 cycles for modified Mt and obtained results showed that modified adsorbent could also be effectively used for anionic pollutant removal from surface water for multiple adsorption-desorption cycles.

adsorption, Montmorillonite, amino acid, anionic pollutant, water

Para citar este artículo

Elham Shokri, Reza Yegani & Borhan Ghofrani, «Preparation of a new modified clay with amino acid for anionic pollutant removal from water», Bulletin de la Société Royale des Sciences de Liège [En ligne], Volume 86 - Année 2017, Special issue, 157 - 164 URL : https://popups.uliege.be/0037-9565/index.php?id=6634.

Acerca de: Elham Shokri

Faculty of Chemical Engineering, Sahand University of Technology, Tabriz, Iran and  Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran

Acerca de: Reza Yegani

Faculty of Chemical Engineering, Sahand University of Technology, Tabriz, Iran and  Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran

Acerca de: Borhan Ghofrani

Faculty of Chemical Engineering, Sahand University of Technology, Tabriz, Iran and  Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran