- Facile Preparation of Mesoporous γ-Alumina Nanoparticles with High-Surface-Area via Sol-Gel Method and their Efficiency for the Removal of Lead from Aqueous Solution
Weergave(s): 762 (12 ULiège)
Download(s): 308 (1 ULiège)
Facile Preparation of Mesoporous γ-Alumina Nanoparticles with High-Surface-Area via Sol-Gel Method and their Efficiency for the Removal of Lead from Aqueous Solution
Documenten bij dit artikel
Version PDF originaleAbstract
In the present investigation, γ-alumina nanoparticles with high specific surface area (351 m2/g) and relatively narrow pore size distribution was prepared using sol-gel method in the presence of aluminum isopropoxide as an aluminum precursor, distilled water, acetic acid as hydrolysis rate controller and tert-butanol as solvent.
The calcined γ-alumina nanoparticles were characterized using X-ray diffractometer (XRD), scanning electron microscope (SEM) and nitrogen adsorption-desorption techniques.
Prepared γ-alumina was tested for the adsorption of Pb2+ from aqueous solution at toxic metal concentrations, and isotherms were determined. The Pb2+ adsorption performance of the as-prepared samples was studied by atomic adsorption spectroscopy (AAS) method.
According to the results, the prepared γ-aluminashowed the great adsorption performance of Pb2+with a high adsorption rate and adsorption capacity of 1150 mg/g when the adsorption reached to equilibrium for 5 min at room temperature and pH=5.5. The adsorbed amount increased rapidly with pH variation from pH 3 to 9. The optimum contact time, initial concentration of adsorbate, adsorbent mass and pH were determined and Langmuir, Freundlich and Tempkin adsorption models were obtained using metal ions concentrations in ranging from 100 to 400 mg/L. Correlation coefficients (R2) of Langmuir, Freundlich and Tempkin adsorption isotherms were 0.9994, 0.9975 and 0.9982, respectively, and Langmuir isotherm was more suitable for adsorption on γ-alumina than others. Also presence of Pb2+ ions has been confirmed by infrared spectroscopy.
Efficient synthesis strategy, exceptionally high specific surface area and high adsorption efficiency of these mesoporous γ-alumina nanoparticles showed an excellent ability to remove Pb2+ heavy metal ions from aqueous solution that could find potential utility in the purification of polluted water.