Quantitative fractography of sintered carbides

(Volume 18 (1999) — Number 1 - May 1999)
Article
Open Access

Documento adjunto(s)

Anexidades

Abstract

Three grades of sintered carbides ("Baildonit" Co Ltd) with diversified tungsten carbide size (0.5-8.0 µm) and cobalt binder (6-9.5 wt. %) were investigated. The specimens were fractured using three points bending device mounted in scanning electron microscope. Values of bending strength and deflection measured this way were used in further fractography analysis. The fractures exhibited gradual change of certain features (from the coarse to fine grained specimens): decrease in transcrystalline fracture fraction, decrease in secondary cracks and WC particles cracks frequency. Confocal laser microscopy (TSC 4D Leica Laser Technik) was used to obtain 3D topography of the fractures and main fractography parameters - average arithmetic profile deviation from the average line (Ra), surface roughness (Rs) and fractal dimension.

Keywords : watersheds.

Para citar este artículo

Janusz Richter, Jan Cwajna & Stanisław Roskosz, «Quantitative fractography of sintered carbides», Acta Stereologica [En ligne], Volume 18 (1999), Number 1 - May 1999, 75-80 URL : https://popups.uliege.be/0351-580x/index.php?id=118.

Acerca de: Janusz Richter

Silesian University of Technology, Department of Materials Science ul. Krasińkiego 8, PL-40-019 Katowice, Poland

Acerca de: Jan Cwajna

Silesian University of Technology, Department of Materials Science ul. Krasińkiego 8, PL-40-019 Katowice, Poland

Acerca de: Stanisław Roskosz

Silesian University of Technology, Department of Materials Science ul. Krasińkiego 8, PL-40-019 Katowice, Poland